Lamart 2104-PC61
Lamart 2104-PC61 is a pressure-sensitive product engineered to your specifications, featuring high tack, high peel, and high shear properties. It offers excellent adhesion to LSE substrates and very good elevated temperature shear resistance. The construction includes a 61# release liner, a 1.5 mil aggressive acrylic PSA, a 0.5 mil PET layer, and a 2.0 mil aggressive acrylic PSA.
This product is designed for applications requiring robust adhesion and shear strength, especially in challenging environments. Users should determine the suitability and fitness for their specific use, assuming all associated risks and liabilities. The seller's liability is limited to the replacement value of the material.
Key Features:
- High Tack, High Peel, High Shear
- Excellent adhesion to LSE substrates
- Very good elevated temperature shear
- 61# release liner
- 1.5 mil aggressive acrylic PSA
- 0.5 mil PET layer
- 2.0 mil aggressive acrylic PSA
Typical Applications:
- Automotive applications
- Aerospace applications
- Electronics applications
- Industrial applications
- Medical applications
- Printing and Graphics applications
Product Key Properties: The product consists of a 61# release liner, a 1.5 mil aggressive acrylic PSA, a 0.5 mil PET layer, and a 2.0 mil aggressive acrylic PSA, providing a multi-layered construction optimized for performance.
Product Performance Benefits: High tack ensures immediate grab; high peel provides strong adhesion; high shear offers resistance to movement under stress; excellent adhesion to LSE substrates expands application possibilities; very good elevated temperature shear maintains bond integrity in high-temperature environments.
Technical Data:
- 180° Peel Adhesion (ozs./inch / N):
- S/S: 20 min. @ RT: 85 / 23, 24 Hrs. @ RT: 110 / 31
- Aluminum: 20 min. @ RT: 83 / 23, 24 Hrs. @ RT: 115 / 32
- Glass: 20 min. @ RT: 80 / 22, 24 Hrs. @ RT: 114/ 32
- Shear Adhesion:
- S/S: 1/2 X 1 X 1000g @ RT: >24 hrs
- Elevated Temperature Shear: 1” X 1” x 500 g @ 70°C: 8 Hrs
- Loop Tack: 4.0 Lbs./in²